Thick film silver paste and its use in the manufacture of semiconductor devices

ABSTRACT

The present invention is directed to an electroconductive silver thick film paste composition comprising Ag particles and a Bi—Cu—B—Zn-based glass frit dispersed in an organic medium. The present invention is further directed to an electrode formed from the paste composition and a semiconductor device and, in particular, a solar cell comprising such an electrode. The paste is particularly useful for forming a tabbing electrode.

FIELD OF THE INVENTION

The present invention is directed primarily to a thick film silver paste composition and thick film silver electrodes, particularly tabbing electrodes, formed from the composition. It is further directed to a silicon semiconductor device and, in particular, it pertains to the electroconductive composition used in the formation of a thick film silver electrode of a solar cell.

TECHNICAL BACKGROUND OF THE INVENTION

The present invention can be applied to a broad range of semiconductor devices, although it is especially effective in light-receiving elements such as photodiodes and solar cells. The background of the invention is described below with reference to solar cells as a specific example of the prior art.

A conventional solar cell structure with a p-type base has a negative electrode that is typically on the front-side or sun side of the cell and a positive electrode on the back side. Radiation of an appropriate wavelength falling on a p-n junction of a semiconductor body serves as a source of external energy to generate hole-electron pairs in that body. Because of the potential difference which exists at a p-n junction, holes and electrons move across the junction in opposite directions and thereby give rise to flow of an electric current that is capable of delivering power to an external circuit. Most solar cells are in the form of a silicon wafer that has been metallized, i.e., provided with metal electrodes that are electrically conductive. Typically thick film pastes are screen printed onto substrate and fired to form the electrodes.

An example of this method of production is described below in conjunction with FIGS. 1A-1F.

FIG. 1A shows a single crystal or multi-crystalline p-type silicon substrate 10.

In FIG. 1B, an n-type diffusion layer 20 of the reverse conductivity type is formed by the thermal diffusion of phosphorus using phosphorus oxychloride as the phosphorus source. In the absence of any particular modifications, the diffusion layer 20 is formed over the entire surface of the silicon p-type substrate 10. The depth of the diffusion layer can be varied by controlling the diffusion temperature and time, and is generally formed in a thickness range of about 0.3 to 0.5 microns. The n-type diffusion layer may have a sheet resistivity of several tens of ohms per square up to about 120 ohms per square.

After protecting the front surface of this diffusion layer with a resist or the like, as shown in FIG. 1C the diffusion layer 20 is removed from the rest of the surfaces by etching so that it remains only on the front surface. The resist is then removed using an organic solvent or the like.

Then, as shown in FIG. 1D an insulating layer 30 which also functions as an anti-reflection coating is formed on the n-type diffusion layer 20. The insulating layer is commonly silicon nitride, but can also be a SiN_(x):H film (i.e., the insulating film comprises hydrogen for passivation during subsequent firing processing), a titanium oxide film, a silicon oxide film, or a silicon oxide/titanium oxide film. A thickness of about 700 to 900 Å of a silicon nitride film is suitable for a refractive index of about 1.9 to 2.0. Deposition of the insulating layer 30 can be by sputtering, chemical vapor deposition, or other methods.

Next, electrodes are formed. As shown in FIG. 1E, a silver paste 500 for the front electrode is screen printed on the silicon nitride film 30 and then dried. In addition, a back side silver or silver/aluminum paste 70, and an aluminum paste 60 are then screen printed onto the back side of the substrate and successively dried. Firing is carried out in an infrared furnace at a temperature range of approximately 750 to 850° C. for a period of from several seconds to several tens of minutes.

Consequently, as shown in FIG. 1F, during firing, aluminum diffuses from the aluminum paste 60 into the silicon substrate 10 on the back side thereby forming a p+ layer 40 containing a high concentration of aluminum dopant. This layer is generally called the back surface field (BSF) layer, and helps to improve the energy conversion efficiency of the solar cell.

Firing converts the dried aluminum paste 60 to an aluminum back electrode 61. The back side silver or silver/aluminum paste 70 is fired at the same time, becoming a silver or silver/aluminum back electrode, 71. During firing, the boundary between the back side aluminum and the back side silver or silver/aluminum assumes the state of an alloy, thereby achieving electrical connection. Most areas of the back electrode are occupied by the aluminum electrode 61, owing in part to the need to form a p+ layer 40. Because soldering to an aluminum electrode is impossible, the silver or silver/aluminum back electrode 71 is formed over portions of the back side as an electrode for interconnecting solar cells by means of copper ribbon or the like. In addition, the front side silver paste 500 sinters and penetrates through the silicon nitride film 30 during firing, and thereby achieves electrical contact with the n-type layer 20. This type of process is generally called “fire through.” The fired electrode 501 of FIG. 1F clearly shows the result of the fire through.

There is an on-going effort to provide thick film paste compositions that have reduced amounts of silver while at the same time maintaining electrical performance and other relevant properties of the resulting electrodes and devices. The present invention provides a silver paste composition that simultaneously provides a system with lower amounts of Ag while still maintaining electrical and mechanical performance.

SUMMARY OF THE INVENTION

The present invention provides a thick film paste composition comprising:

-   -   (a) 35-45 wt % silver, said silver consisting essentially of         spherical silver particles with d₅₀<1 μm;     -   (b) 0.5-6 wt % Pb-free bismuth-copper-boron-zinc-based-oxide         glass frit; and     -   (c) organic medium;         wherein said silver and said glass frit are dispersed in said         organic medium and wherein the wt % are based on the total         weight of said paste composition, said Ph-free         bismuth-copper-boron-zinc-based-oxide glass frit comprising         70-80 wt % Bi₂O₃, 5-11 wt %, CuO, 3-8 wt % B₂O₃ and 3-8 wt %         ZnO, wherein the oxide wt% are based on the total weight of said         Pb-free bismuth-copper-boron-zinc-based-oxide glass frit.

In one embodiment the Pb-free bismuth-copper-boron-zinc-based-oxide glass frit further comprises 2-6 wt % SiO₂ and 0.1-1.5 wt % Al₂O₃, wherein the oxide wt % are based on the total weight of the Pb-free bismuth-copper-boron-zinc-based-oxide glass frit.

The invention also provides a semiconductor device, and in particular, a solar cell comprising an electrode formed from the instant paste composition, wherein the paste composition has been fired to remove the organic medium and form the electrode.

BRIEF DESCRIPTION OF THE FIGURES

FIGS. 1A-1F illustrate the fabrication of a semiconductor device. Reference numerals shown in FIG. 1 are explained below.

-   -   10: p-type silicon substrate     -   20: n-type diffusion layer     -   30: silicon nitride film, titanium oxide film, or silicon oxide         film     -   40: p+ layer (back surface field, BSF)     -   60: aluminum paste formed on back side     -   61: aluminum back side electrode (obtained by firing back side         aluminum paste)     -   70: silver/aluminum paste formed on back side     -   71: silver/aluminum back side electrode (obtained by firing back         side silver/aluminum paste)     -   500: silver paste formed on front side     -   501: silver front electrode (formed by firing front side silver         paste)

FIGS. 2 A-D explain the manufacturing process of one embodiment for manufacturing a solar cell using the electroconductive paste of the present invention. Reference numerals shown in FIG. 2 are explained below.

-   -   102 silicon substrate with diffusion layer and an         anti-reflection coating     -   104 light-receiving surface side electrode     -   106 paste composition for Al electrode     -   108 paste composition of the invention for tabbing electrode     -   110 Al electrode     -   112 tabbing electrode

DETAILED DESCRIPTION OF THE INVENTION

The conductive thick film paste composition of the instant invention contains a reduced amount of silver but provides the ability to form an electrode from the paste wherein the electrode simultaneously has good electrical and adhesion properties.

The conductive thick film paste composition comprises silver, a Pb-free bismuth-copper-boron-zinc-based-oxide glass frit, and an organic medium. It is used to form screen printed electrodes and, particularly, to form tabbing electrodes on the back side on the silicon substrate of a solar cell. The paste composition comprises 35-55 wt % silver, 0.5-6 wt % glass frit, and organic medium, wherein the silver and the glass frit are dispersed in the organic medium and wherein the weight percentages are based on the total weight of the paste composition.

Each component of the thick film paste composition of the present invention is explained in detail below.

Silver

In the present invention, the conductive phase of the paste is silver (Ag). The silver consists essentially of spherical silver particles with d₅₀<1 μm, wherein the median particle diameter, d₅₀ is determined by means of laser diffraction. The d₅₀ represents the median or 50th percentile of the particle size distribution as measured by volume. That is, the d₅₀ is a value on the distribution such that 50% of the particles have a volume of this value or less. In one embodiment, the silver consists essentially of spherical silver particles with d₅₀<0.5 μm.

The silver particles are not perfect spheres but have a generally spherical shape and are referred to herein as “spherical”.

As a result of its cost, it is advantageous to reduce the amount of silver in the paste while maintaining the required properties of the paste and the electrode formed from the paste. In addition, the instant thick film paste enables the formation of electrodes with reduced thickness, resulting in further savings. The instant thick film paste composition comprises 35-45 wt % silver, based on the total weight of the paste composition. In one embodiment the thick film paste composition comprises 38-42 wt % silver.

Glass Frit

The glass frit used in forming the instant composition is a Ft-free bismuth-copper-boron-zinc-based-oxide (Bi—Cu—B—Zn-based oxide) glass frit. In one embodiment the composition contains 0.5-6 wt % glass frit, wherein the wt % is based on the total weight of the composition. In another embodiment the composition contains 0.2-5 wt % glass frit, wherein the wt % is based on the total weight of the composition.

Glass compositions, also termed glass frits, are described herein as including percentages of certain components. Specifically, the percentages are the percentages of the components used in the starting material that was subsequently processed as described herein to form a glass composition. Such nomenclature is conventional to one of skill in the art. In other words, the composition contains certain components, and the percentages of those components are expressed as a percentage of the corresponding oxide form. As recognized by one of ordinary skill in the art in glass chemistry, a certain portion of volatile species may be released during the process of making the glass. An example of a volatile species is oxygen. It should also be recognized that while the glass behaves as an amorphous material it will likely contain minor portions of a crystalline material.

If starting with a fired glass, one of ordinary skill in the art may calculate the percentages of starting components described herein using methods known to one of skill in the art including, but not limited to: Inductively Coupled Plasma-Mass Spectroscopy (ICP-MS), Inductively Coupled Plasma-Atomic Emission Spectroscopy (ICP-AES), and the like. In addition, the following exemplary techniques may be used: X-Ray Fluorescence spectroscopy (XRF); Nuclear Magnetic Resonance spectroscopy (NMR); Electron Paramagnetic Resonance spectroscopy (EPR); Mössbauer spectroscopy; electron microprobe Energy Dispersive Spectroscopy (EDS); electron microprobe Wavelength Dispersive Spectroscopy (WDS); or Cathodo-Luminescence (CL).

One of ordinary skill in the art would recognize that the choice of raw materials could unintentionally include impurities that may be incorporated into the glass during processing. For example, the impurities may be present in the range of hundreds to thousands ppm. The presence of the impurities would not alter the properties of the glass, the composition, e.g. a thick-film composition, or the fired device. For example, a solar cell containing a thick-film composition may have the efficiency described herein, even if the thick-film composition includes impurities. “Lead-free” as used herein means that no lead has been intentionally added.

The glass frit may be prepared by mixing the oxides to be incorporated therein (or other materials that decompose into the desired oxides when heated, e.g., fluorides) using techniques understood by one of ordinary skill in the art. Such preparation techniques may involve heating the mixture in air or an oxygen-containing atmosphere to form a melt, quenching the melt, and grinding, milling, and/or screening the quenched material to provide a powder with the desired particle size. Melting the mixture of bismuth, copper, boron, zinc and other oxides to be incorporated therein is typically conducted to a peak temperature of 950 to 1200° C. The molten mixture can be quenched, for example, on a stainless steel platen or between counter-rotating stainless steel rollers to form a platelet. The resulting platelet can be milled to form a powder. Typically, the milled powder has a d₅₀ of 0.1 to 3.0 microns as measured with a Microtrac S3500. One skilled in the art of producing glass frit may employ alternative synthesis techniques such as but not limited to water quenching, sol-gel, spray pyrolysis, or others appropriate for making powder forms of glass.

The oxide product of the above process is typically essentially an amorphous (non-crystalline) solid material, i.e., a glass. However, in some embodiments the resulting oxide may be amorphous, partially amorphous, partially crystalline, crystalline or combinations thereof. As used herein “glass frit” includes all such products.

The starting mixture used to make the Bi—Cu—B—Zn-based oxide includes 70-80 wt % Bi₂O₃, 5-11 wt % CuO, 3-8 wt % B₂O₃ and 3-8 wt % ZnO, wherein the oxide wt % are based on the total weight of the Pb-free bismuth-copper-boron-zinc-based-oxide glass frit. In one such embodiment the Bi—Cu—B—Zn-based oxide also contains 2-6 wt % SiO₂ and 0.1-1.5 wt % Al₂O₃.

In another embodiment, the Bi—Cu—B—Zn-based oxide includes 72-78 wt % Bi₂O₃, 7-11 wt % CuO, 3-8 wt % B₂O₃ and 3-8 wt % ZnO, wherein the oxide wt % are based on the total weight of the Pb-free bismuth-copper-boron-zinc-based-oxide glass frit. In one such embodiment the Bi—Cu—B—Zn-based oxide also contains 3-5 wt % SiO₂ and 0.5-1.5 wt % Al₂O₃.

In one embodiment, the Bi—Cu—B—Zn-based oxide consists essentially of 70-80 wt % Bi₂O₃, 5-11 wt % CuO, 3-8 wt % B₂O₃, 3-8 wt % ZnO, 2-6 wt % SiO₂ and 0.1-1.5 wt % Al₂O₃, wherein the oxide wt % are based on the total weight of the Pb-free bismuth-copper-boron-zinc-based-oxide glass frit.

In any of the above embodiments, the oxide may be a homogenous powder. In a further embodiment, the oxide may be a combination of more than one powder, wherein each powder may separately be a homogenous population. The composition of the overall combination of the 2 powders is within the ranges described above. For example, the oxide may include a combination of 2 or more different powders; separately, these powders may have different compositions, and may or may not be within the ranges described above; however, the combination of these powders may be within the ranges described above.

In any of the above embodiments, the oxide composition may include one powder which includes a homogenous powder including some but not all of the desired elements of the oxide composition, and a second powder, which includes one or more of the other desired elements. In an aspect of this embodiment, the powders may be melted together to form a uniform composition. In a further aspect of this embodiment, the powders may be added separately to a thick film composition.

Organic Medium

The inorganic components of the thick-film paste composition are mixed with an organic medium to form viscous pastes having suitable consistency and rheology for printing. A wide variety of inert viscous materials can be used as the organic medium. The organic medium can be one in which the inorganic components are dispersible with an adequate degree of stability during manufacturing, shipping and storage of the pastes, as well as on the printing screen during the screen-printing process.

Suitable organic media have rheological properties that provide stable dispersion of solids, appropriate viscosity and thixotropy for screen printing, appropriate wettability of the substrate and the paste solids, a good drying rate, and good firing properties. The organic medium can contain thickeners, stabilizers, surfactants, and/or other common additives. One such thixotropic thickener is thixatrol. The organic medium can be a solution of polymer(s) in solvent(s). Suitable polymers include ethyl cellulose, ethylhydroxyethyl cellulose, wood rosin, mixtures of ethyl cellulose and phenolic resins, polymethacrylates of lower alcohols, and the monobutyl ether of ethylene glycol monoacetate. Suitable solvents include terpenes such as alpha- or beta-terpineol or mixtures thereof with other solvents such as kerosene, dibutylphthalate, butyl carbitol, butyl carbitol acetate, hexylene glycol and alcohols with boiling points above 150° C., and alcohol esters. Other suitable organic medium components include: bis(2-(2-butoxyethoxy)ethyl adipate, dibasic esters such as DBE, DBE-2, DBE-3, DBE-4, DBE-5, DBE-6, DBE-9, and DBE 1B, octyl epoxy tallate, isotetradecanol, and pentaerythritol ester of hydrogenated rosin. The organic medium can also comprise volatile liquids to promote rapid hardening after application of the thick-film paste composition on a substrate.

The optimal amount of organic medium in the thick-film paste composition is dependent on the method of applying the paste and the specific organic medium used. The instant thick-film paste composition contains 35 to 60 wt % of organic medium, based on the total weight of the paste composition.

If the organic medium comprises a polymer, the polymer typically comprises 8 to 15 wt % of the organic composition.

Preparation of the Thick Film Paste Composition

In one embodiment, the thick film paste composition can be prepared by mixing Ag powder, the glass frit powder, and the organic medium and in any order. In some embodiments, the inorganic materials are mixed first, and they are then added to the organic medium. In other embodiments, the Ag powder which is the major portion of the inorganics is slowly added to the organic medium. The viscosity can be adjusted, if needed, by the addition of solvents. Mixing methods that provide high shear are useful. The thick film paste contains less than 55 wt % of inorganic components, i.e., the Ag powder, the glass frit powder and any inorganic additives, based on the total weight of the paste composition. In an embodiment the thick film paste contains less than 50 wt % of these inorganic components.

The thick film paste composition can be deposited by screen-printing, plating, extrusion, inkjet, shaped or multiple printing, or ribbons.

In this electrode-forming process, the thick film paste composition is first dried and then heated to remove the organic medium and sinter the inorganic materials. The heating can be carried out in air or an oxygen-containing atmosphere. This step is commonly referred to as “firing.” The firing temperature profile is typically set so as to enable the burnout of organic binder materials from the dried thick film paste composition, as well as any other organic materials present. In one embodiment, the firing temperature is 750 to 950° C. The firing can be conducted in a belt furnace using high transport rates, for example, 100-500 cm/min, with resulting hold-up times of 0.05 to 5 minutes. Multiple temperature zones, for example 3 to 11 zones, can be used to control the desired thermal profile.

An example in which a solar cell is prepared using the paste composition of the present invention as a tabbing electrode on the back side of the solar cell is explained with reference to FIGS. 2A-2D.

First, a Si substrate 102 with a diffusion layer and an anti-reflection coating is prepared. On the light-receiving front side face (surface) of the Si substrate, electrodes 104 typically mainly composed of Ag are installed as shown in FIG. 2A. On the back face of the substrate, aluminum paste, for example, PV333, PV322 (commercially available from the DuPont co., Wilmington, Del.), is spread by screen printing and then dried 106 as shown in FIG. 2B. The paste composition of the present invention is then spread in a partially overlapped state with the dried aluminum paste and is then dried 108 as shown in FIG. 2C. The drying temperature of each paste is preferably 150° C. or lower. Also, the overlapped part of the aluminum paste and the paste of the invention is preferably about 0.5-2.5 mm.

Next, the substrate is fired at a temperature of 700-950° C. for about 1-15 min so that the desired solar cell is obtained as shown in FIG. 2D. The electrodes 112 are formed from the paste composition of the present invention wherein the composition has been fired to remove the organic medium and sinter the inorganics. The solar cell obtained has electrodes 104 on the light-receiving front side of the substrate 102, and Al electrodes 110 mainly composed of Al and electrodes 112 composed of the fired paste composition of the present invention on the back face. The electrodes 112 serve as a tabbing electrode on the back side of the solar cell.

EXAMPLES Example 1 Bismuth-Copper-Boron-Zinc-Based Oxide Preparation

A bismuth-copper-boron-zinc-based oxide composition was prepared by mixing and blending Bi₂O₃, CuO, B₂O₃, ZnO, SiO₂ and Al₂O₃ powders to result in a Bi—Cu—B—Zn-based oxide composition comprising 76.30 wt % Bi₂O₃, 8.0 wt % CuO, 5.0 wt % B₂O₃, 5.6 wt % ZnO, 4.50 wt % SiO₂, and 0.9 wt % Al₂O₃ based on the total weight of the bismuth-copper-boron-zinc-based oxide.

The blended powder batch materials were loaded to a platinum alloy crucible then inserted into a furnace and heated at 900° C. in air or O₂ for one hour to melt the mixture. The liquid melt was quenched from 900° C. by removing the platinum crucible from the furnace and pouring the melt through counter rotating a stainless steel rollers gapped to 0.010-0.020″. The resulting material was coarsely crushed in a stainless steel container. The crushed material was then ball-milled in an alumina-silicate ceramic ball mill with zirconia media and water until the d₅₀ was 0.5-0.7 microns. The ball-milled material was then separated from the milling balls, wet screened and dried by hot air oven. The dried powder was run through a 200 mesh screen to provide the Bi—Cu—B—Zn-based oxide powder used in the thick film paste preparations. X-ray analysis of the powder showed a characteristic of an amorphous material. The material was characterized by Differential-Thermal Analysis (DTA) and shows an onset of particle sintering at 300-320° C. Pellet fusion testing shows viscous flow starting at 350-400° C. The liquidus for the composition appears to be near 510° C. (between 320° C. and 510° C. some crystalline phases may be transiently formed and re-dissolved in the region between sintering onset and the liquidus temperature).

Example 2 Bismuth-Copper-Boron-Zinc-Based Oxide Preparation

A second bismuth-copper-boron-zinc-based oxide composition was prepared by mixing and blending Bi₂O₃, CuO, B₂O₃, ZnO, SiO₂ and Al₂O₃ powders to result in a Bi—Cu—B—Zn- based oxide composition comprising 73.30 wt % Bi₂O₃, 9.21 wt % CuO, 5.40 wt % B₂O₃, 6.45 wt % ZnO, 4.66 wt % SiO₂, and 0.99 wt % Al₂O₃ based on the total weight of the bismuth-copper-boron-zinc-based oxide.

The blended powder batch materials were processed essentially as described in Example 1 to provide the Bi—Cu—B—Zn-based oxide powder. 

What is claimed is:
 1. A thick film paste composition comprising: (a) 35-45 wt % of a conductive phase consisting of spherical silver particles with d₅₀<1 μm; (b) 0.5-6 wt % Pb-free bismuth-copper-boron-zinc-based-oxide glass frit; and (c) organic medium; wherein said silver and said glass frit are dispersed in said organic medium and wherein the wt % are based on the total weight of said paste composition, said Pb-free bismuth-copper-boron-zinc-based-oxide glass frit comprising 70-80 wt % Bi₂O₃, 5-11 wt % CuO, 3-8 wt % B₂O₃ and 3-8 wt % ZnO, wherein the oxide wt % are based on the total weight of said Pb-free bismuth-copper-boron-zinc-based-oxide glass frit.
 2. The thick film paste composition of claim 1, said Pb-free bismuth-copper-boron-zinc-based-oxide glass frit further comprising 2-6 wt % SiO₂ and 0.1-1.5 wt % Al₂O₃, wherein the oxide wt % are based on the total weight of said Pb-free bismuth-copper-boron-zinc-based-oxide glass frit.
 3. A semiconductor device comprising an electrode formed from the paste composition of claim 2, wherein said paste composition has been fired to remove the organic medium and form said electrode.
 4. A solar cell comprising an electrode formed from the paste composition of claim 2, wherein said paste composition has been fired to remove the organic medium and form said electrode.
 5. The solar cell of claim 4, wherein said electrode is a tabbing electrode on the back side of said solar cell.
 6. The thick film paste composition of claim 1, said Pb-free bismuth-copper-boron-zinc-based-oxide glass frit comprising 72-78 wt % Bi₂O₃, 7-11 wt % CuO, 3-8 wt % B₂O₃ and 3-8 wt % ZnO, wherein the oxide wt% are based on the total weight of said Pb-free bismuth-copper-boron-zinc-based-oxide glass frit.
 7. A semiconductor device comprising an electrode formed from the paste composition of claim 6, wherein said paste composition has been fired to remove the organic medium and form said electrode.
 8. A solar cell comprising an electrode formed from the paste composition of claim 6, wherein said paste composition has been fired to remove the organic medium and form said electrode.
 9. The solar cell of claim 8, wherein said electrode is a tabbing electrode on the back side of said solar cell.
 10. The thick film paste composition of claim 6, said Pb-free bismuth-copper-boron-zinc-based-oxide glass frit further comprising 3-5 wt % SiO₂ and 0.5-1.5 wt % Al₂O₃, wherein the oxide wt % are based on the total weight of said Pb-free bismuth-copper-boron-zinc-based-oxide glass frit.
 11. A semiconductor device comprising an electrode formed from the paste composition of claim 10, wherein said paste composition has been fired to remove the organic medium and form said electrode.
 12. A solar cell comprising an electrode formed from the paste composition of claim 10, wherein said paste composition has been fired to remove the organic medium and form said electrode.
 13. The solar cell of claim 12, wherein said electrode is a tabbing electrode on the back side of said solar cell.
 14. A semiconductor device comprising an electrode formed from the paste composition of claim 1, wherein said paste composition has been fired to remove the organic medium and form said electrode.
 15. A solar cell comprising an electrode formed from the paste composition of claim 1, wherein said paste composition has been fired to remove the organic medium and form said electrode.
 16. The solar cell of claim 15, wherein said electrode is a tabbing electrode on the back side of said solar cell. 